Effect of combination dope composition and evaporation time on the separation performance of cellulose acetate membrane for demak brackish water treatment

Effect of combination dope composition and evaporation time on the separation performance of cellulose acetate membrane for demak brackish water treatment

Blog Article

The coastal areas in Indonesia often have a problem of clean water lack, because the water is classified as brackish water.Therefore, this research investigated the fabrication of CA membranes using phase inversion method for brackish water treatment.Investigation was conducted to study the effect of combination dope composition and evaporation time on separation performance and morphology of the memrbane.

Membrane was fabricated Rack by dry-wet phase inversion technique with variation of polymer concentration 17, 18 and 20 wt% in the total solid and evaporation time of 5, 10 and 15 seconds, respectively.The asymmetric membranes were characterized by permeability test through rejection and flux measurements using brackish water as feed.The experimental results from SEM images analysis showed that all the membranes have a NEFF U2ACM7HN0B N50 Built In 59cm A/B Electric Double Oven Stainless Steel thin small porous layer and thicker sub-structure of larger porous layer formed asymmetric membrane.

Moreover, the greater polymer concentration is resulting smaller pore size and smaller membrane porosity.The longer evaporation time was also resulted in denser membrane active layer.The best membrane performance was observed at the composition of 20 wt% CA polymer, 1 wt % polyethylene glycol with the solvent evaporation time of 15 seconds.